A335 P11 Paip Keluli Aloi
Oct 20, 2023
A335 P11 Paip Keluli Aloi
SA 335 gr P11 Komposisi Kimia Paip Lancar
| C, % | Mn, % | P, % | S, % | Si, % | Cr, % | Mo, % |
| 0.015 maks | 0.30-0.60 | 0.025 maks | 0.025 maks | 0.50 maks | 4.00-6.00 | 0.45-0.65 |
Ciri Paip Keluli ASTM A335 P11
| Kekuatan Tegangan, MPa | Kekuatan Hasil, MPa | Pemanjangan, % |
| 415 min | 205 min | 30 min |
Carta Tegangan Paip Kimpalan Keluli Aloi P11
| Paip Lancar | ||||||
| P5 | P9 | P11 | P22 | P91 | ||
| Kekuatan Tegangan, minimum., psi | ||||||
| KSI | 60 | 60 | 60 | 60 | 85 | |
| Mpa | 415 | 415 | 415 | 415 | 585 | |
| Kekuatan Hasil, minimum., psi | ||||||
| KSI | 30 | 30 | 30 | 30 | 60 | |
| MPa | 205 | 205 | 205 | 205 | 415 | |