Paip Lancar ASTM A335 P5

Paip Chrome Moly: ASTM A335 / ASME SA335 Gred P5
Jenis fabrikasi: Paip Keluli Lancar
Kandungan Chrome 4.00 % hingga 6.00%, Molibdenum 0.45 hingga 0.65%.
Julat Bekalan: 1/2" hingga 36" DN25 hingga DN900
Ketebalan dinding sehingga SCH 160
Panjang: SRL, DRL, Panjang Tetap
Rawatan permukaan: Digilap, Bersalut 3LPE atau FBE

Jadual Paip Tekanan Tinggi ASME SA 335 Gred P5

OD x Ketebalan(mm)	OD x Ketebalan(mm)	OD x Ketebalan(mm)
38.1 x 3.2	57.0 x 4.9	76.2 x 4.0
38.1 x 4.0	57.0 x 6.3	76.2 x 5.0
38.1 x 6.3	57.0 x 7.9	76.2 x 6.3
42.4 x 3.2	60.3 x 3.2	82.5 x 4.5
42.4 x 4.0	60.3 x 3.6	88.9 x 3.2
44.5 x 3.2	60.3 x 5.0	88.9 x 3.6
44.5 x 6.3	63.5 x 3.2	88.9 x 4.0
48.3 x 3.2	63.5 x 3.6	101.6 x 3.6
48.3 x 3.6	63.5 x 4.0	101.6 x 4.5
50.8 x 4.5	63.5 x 6.3	101.6 x 6.3
51.0 x 3.2	63.5 x 7.9	114.3 x 3.6
51.0 x 3.6	70.0 x 3.2	114.3 x 5.0
51.0 x 6.3	70.0 x 3.6	139.7 x 4.0
57.0 x 3.2	70.0 x 6.3	139.7 x 5.0
57.0 x 3.6	76.2 x 3.6	139.7 x 6.3

p5 Carta Ketebalan Paip Keluli Aloi

NPS [DN] Designator	Toleransi, % daripada Ditentukan
Berakhir	Di bawah
1/8 hingga 2 1/2 [6 hingga 65] termasuk, semua nisbah t/D	20.0%	12.5%
Di atas 2 1/2 [65], t/D < atau=5%	22.5%	12.5%
Di atas 2 1/2 [65], t/D > 5%	15.0%	12.5%
(t=Ketebalan Dinding Ditentukan; D=Diameter Luar Ditentukan)

Carta Komposisi Paip Kimpalan ASTM A335 P5

Keluli Aloi P5	C	Cr	S	Si	Mn	Mo	P
	0.05 – 0.15	1.00 – 1.50	0.025 maks	0.50 – 1.00	0.30 – 0.60	0.44 – 0.65	0.025 maks

Carta Sifat Mekanikal Paip Gred P5 Keluli Aloi

Kekuatan Tegangan, MPa	Kekuatan Hasil, MPa	Pemanjangan
415 min	205 min	30 min